GC Gold Label 9

• Chemical adhesion to tooth structure allows minimal cavity preparation without the need for etching or bonding agents
• Chemical setting without shrinkage allows single step placement without layering
• Similar thermal expansion as tooth structure produce minimal stress on the marginal seal
• Strontium based glass provides good radiopacity and snap-set characteristics unanimously preferred by clinicians
• Strontium based fluoride releasing formulation contributes to internal remineralization within tooth structure as well as increasing surface strength over time
• High compressive and flexural strength, and 60% higher wear resistance than conventional glass ionomers makes Gold Label 9 strong enough for use in posterior teeth

• Class I and small Class II restorations in non-load bearing areas
• Class I and Class II restorations in deciduous teeth
• Transitional restorations
• Base / Core build-ups

• After conditioning the tooth surface with GC Dentin Conditioner (10% polyacrylic acid), apply the Gold Label 9 or Fuji IX GP in Capsule mixed accordingly into the cavity
• Form the contour and place a matrix if required during the working time
• After initial set, when the material starts to lose the glossy appearance, moisture protectwith GC Cocoa Butter or GC Fuji Varnish or GC Fuji Coat LC
• Final finishing under water spray can be carried out at the recommended times from start of mix
• After finishing, apply a final coat of GC Fuji Varnish or GC Fuji Coat LC as a protective coating.

Alternatively, application of a final protective coat of G-Coat PLUS can improve wear resistance

* Mixing conditions at 23°C. Higher temperatures will shorten working time.